Gwoup endistri espesyalize nan envantè asye pur baton fil klere pou divès kalite itilizasyon.

Nou ka fabrike divès kalite baton fil asye pur ak teknik pwosesis diferan.


Estanda:

AISI, ASTM, DIN, EN, GB ak JIS


Materyèl:

300series: 301,302,303,304,304L, 309,309s, 310,310S, 316,316L, 316Ti, 317L, 321,347,

200series: 201,202,202cu, 204;

400series: 409,409L, 410,420,430,431,440;

Lòt moun: 2205,2507,2906,330,660,630,631,17-4ph, 17-7 ph, 904L, elatriye.


Sifas: marinated, poli, elektwo-polish

Kondisyon: mou, semi-mou ak fil difisil

Tretman teknik: hot-rolle & / cold-drawn

Dyamèt: 3 a 20mm


Anbalaj:

3mm a 12mm fil asye pur ka itilize anbalaj bobin dyamèt anndan: 400, 500, 600 ak 650mm

Pwa: 30 a 1200kg (vlope ak fim deyò)


Karakteristik:

Kondisyon sifas ki inifòm ak bèl

Excellent kapasite kap fòme bobin

Segondè Elastisite ak gwo fatig ki reziste

Bonjan rezistan kont kòw


Aplikasyon:

Itilize pou prentan, vis, kòd, kab ak fil long

Fil fè desen, tissage, kawoutchou, en fe ak tretman medikal

Klou grenn, vis, boulon, nwa ak ekipman segondè filtraj presizyon

Apwopriye pou ekipman pou bisiklèt, kwizin ak sanitasyon, etajè machandiz yo, kaj pou bèt kay

manch dekoratif ak panyen, manje ak Pwodwi pou Telefòn machin medikal

Kalite Klas Klas Eleman chimik%
C Cr Ni Mn P S Mo Si Cu N Lòt
Austenitic 201 SUS201 ≤0.15 16.00-18.00 3.50-5.50 5.50-7.50 ≤0.060 ≤0.030 - ≤1.00 - ≤0,25 -
202 SUS202 ≤0.15 17.00-19.00 4.00-6.00 7.50-10.00 ≤0.060 ≤0.030
≤1.00 - ≤0,25 -
301 1.4310 ≤0.15 16.00-18.00 6.00-8.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - ≤0.10 -
302 1Cr18Ni9 ≤0.15 17.00-19.00 8.00-10.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - ≤0.10 -
303 1.4305 ≤0.15 17.00-19.00 8.00-10.00 ≤2.00 ≤0,20 ≤0.030 - ≤1.00 - - -
303se Y1Cr18Ni9Se ≤0.15 17.00-19.00 8.00-10.00 ≤2.00 ≤0,20 ≤0.030 - ≤1.00 - - Se 0.15
304 1.4301 ≤0,77 17.00-19.00 8.00-10.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - -
304L 1.4307 ≤0.030 18.00-20.00 8.00-10.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - -
304H 1.4948 0.04-0.10 18.00-20.00 8.00-10.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - -
305 * ≤0.12 17.00-19.00 11.00-13.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - -
308 * ≤0.08 19.00-21.00 10.00-12.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - -
309 1.4828 ≤0,20 22.00-24.00 12.00-15.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - -
309S * ≤0.08 22.00-24.00 12.00-15.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - -
310 1.4842 ≤0,25 24.00-26.00 19.00-22.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.50 - - -
310S * ≤0.08 24.00-26.00 19.00-22.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.50 - - -
314 1.4841 ≤0,25 23.00-26.00 19.00-22.00 ≤2.00 ≤0.045 ≤0.030 - 1.50-3.00 - - -
316 1.4401 ≤0.08 16.00-18.50 10.00-14.00 ≤2.00 ≤0.045 ≤0.030 2.00-3.00 ≤1.00 - - -
316L 1.4404 ≤0.030 16.00-18.00 10.00-14.00 ≤2.00 ≤0.045 ≤0.030 2.00-3.00 ≤1.00 - - -
316Ti 1.4571 ≤0.08 16.00-18.00 10.00-14.00 ≤2.00 ≤0.045 ≤0.030 2.00-3.00 ≤1.00 - 0.1 Ti5 (C + N) ~ 0.70
317 * ≤0.08 18.00-20.00 11.00-15.00 ≤2.00 ≤0.045 ≤0.030 3.00-4.00 ≤1.00 - 0.1 -
317L 1.4438 ≤0.03 18.00-20.00 11.00-15.00 ≤2.00 ≤0.045 ≤0.030 3.00-4.00 ≤1.00 - 0.1 -
321 1.4541 ≤0.08 17.00-19.00 9.00-12.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - Ti5 (C + N) ~ 0.70
321H * 0.04-0.10 17.00-19.00 9.00-12.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - Ti5 (C + N) ~ 0.70
347 1.4550 ≤0.08 17.00-19.00 9.00-12.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - Nb≥10 * C% -1.10
347H 1.494 0.04-0.10 17.00-19.00 9.00-12.00 ≤2.00 ≤0.045 ≤0.030 - ≤1.00 - - Nb≥10 * C% -1.10
xm-19 Nitronic50 ≤0,66 20.50-23.50 11.50-13.50 4.0-6.0 ≤0.045 ≤0.030 1.50-3.00 ≤1.00 - 0.2-0.4

Nb: 0.10-0.30

V: 0.10-0.30

904L N08904 ≤0.02 19.0-23.0 23.0-28.0 4.0-5.0 ≤0.045 ≤0.035
≤1.00
0.1 Cu: 1.0-2.0
Duplex 2205 S32205 ≤0.03 22.0-23.0 4.5-6.5 ≤2.00 ≤0.030 ≤0.020 3.0-3.5 ≤1.00 - 0.14-0.20
2507 S32750 ≤0.03 24.0-26.0 6.0-8.0 ≤1.20 ≤0.035 ≤0.020 3.0-5.0 ≤0.80 0.5 0.24-0.32
* S32760 ≤0.03 24.0-26.0 6.0-8.0 ≤1.00 ≤0.030 ≤0.010 3.0-4.0 ≤1.00 0.5-1.00 0.2-0.3
2304 S32304 ≤0.03 21.5-24.5 3.0-5.5 ≤2.50 ≤0.040 ≤0.030 0.05-0.6 ≤1.00 0.05-0.6 0.05-0.2
329 1.4460 ≤0.08 23.00-28.00 2.00-5.00 ≤1.00 ≤0.040 ≤0.030 1.00-2.00 ≤0,75 - -
Ferit 409 S40900 ≤0.03 10.50-11.70 0.5 ≤1.00 ≤0.040 ≤0.020 - ≤1.00 - ≤0.030

Ti6 (C + N) ~ 0.50

Nb: 0.17

430 1Cr17 ≤0.12 16.00-18.00 - ≤1.0 ≤0.040 ≤0.030 - ≤1.0 - - -
430F Y1Cr17 ≤0.12 16.00-18.00 - ≤1.25 ≤0.060 ≥0.15 - ≤1.00 - - -
444 S44400 ≤0.025 17.50-19.50 1 ≤1.00 ≤0.040 ≤0.030 1.75-2.5 ≤1.00 - 0.035 Ti + Nb: 0.2 + 4 (C + N) ~ 0.80
446 S44600 ≤0,20 23.00-27.00 0.75 ≤1.5 ≤0.040 ≤0.030 1.50-2.50 ≤1.00 - ≤0,25 -
Martensite 410 1Cr13 0.08-0.15 11.50-13.50 0.75 ≤1.00 ≤0.040 ≤0.030 - ≤1.00 - - -
410S * ≤0.080 11.50-13.50 0.6 ≤1.00 ≤0.040 ≤0.030 - ≤1.00 - - -
416 Y1Cr13 ≤0.15 12.00-14.00 3) ≤1.25 ≤0.060 ≥0.15 - ≤1.00 - - -
420 2Cr13 ≥0.15 12.00-14.00 - ≤1.00 ≤0.040 ≤0.030 - ≤1.00 - - -
420J2 3Cr13 0.26-0.35 12.00-14.00 - ≤1.00 ≤0.040 ≤0.030 - ≤1.00 - - -
420F Y3Cr13 0.30-0.40 12.00-14.00 0.5 ≤1.25 ≤0.060 ≥0.15 - ≤1.00 0.6 - -
* 4Cr13 0.36-0.45 12.00-14.00 3) ≤0.80 ≤0.040 ≤0.030 - ≤0.60 - - -
431 1Cr17Ni2 ≤0,20 15.00-17.00 1.50-2.50 ≤1.00 ≤0.040 ≤0.030 - ≤0.80 - - -
440C 11Cr17 0.95-1.20 16.00-18.00 - ≤1.00 ≤0.040 ≤0.030 0.75 ≤1.00 - - -
PH 630 17-4PH ≤0,77 15.00-17.50 3.00-5.00 ≤1.00 ≤0.035 ≤0.030 - ≤1.00 3.00-5.00 - Nb 0.15-0.45
631 17-7PH ≤0.09 16.00-18.00 6.50-7.50 ≤1.00 ≤0.035 ≤0.030 - ≤1.00 ≤0.50 - Al 0.75-1.50
632 15-5PH ≤0.09 14.00-16.00 3.50-5.50 ≤1.00 ≤0.040 ≤0.030 2.00-3.00 ≤1.00 2.5-4.5 - Al 0.75-1.50


Ak eksperyans lajè ak ekspètiz, Beall Industry Group se youn nan dirijan en fe manifaktirè yo baton briyan ak founisè. Nou gen dè santèn de wo-kalifye travayè nan sèvis ou. Tanpri, asire w ke ou jwenn pri konpetitif asye pur fe fil baton an pou vann avèk nou.